| Category | Sr.No. | Name of Test | Test Method |
|---|---|---|---|
| Resins, Plastics, Polymers, Paints & varnishes | 1 | Viscosity by Brookfield Viscometer | ASTM D 2196 – 10 |
| 2 | Viscosity by flow cup | IS 101 (Part 1 / sec 5) –R-2006;ASTM D 1200 -94 – 2005 | |
| 3 | Specific Gravity | IS 101 (Part 1 / sec 7) –R-2006 | |
| 4 | Gel Time | ISO 9396, IS 6746 -1972 (FF/TM-04) | |
| 5 | Drying time | IS 101 (Part 3/sec 1) – 1986,IS:10026 (Part 2) – 1999 | |
| 6 | Ability to cure in considerable thickness | IEC 60464 -2-2001-07;IS 10026 (Part 2)-1999; | |
| 7 | Acid Value | IS 101 (Part 9 /sec 1)-2006 | |
| 8 | Amine Value | ISO -9702-1996 | |
| 9 | Epoxy equivalent | ISO 3001 / ASTM D1652 -11 | |
| 10 | Easily hydrolysable Chorine Content | ASTM D 1726 – 11 | |
| 11 | Viscosity by falling ball viscometer | ISO 12058-1-97-E | |
| 12 | High-shear viscosity using cone/plate viscometer | ASTM D 4287 – 00-2010 | |
| 13 | Thixotropic Index | ASTM D 4287 – 00-2010 | |
| 14 | Ionic Chlorine Content | ISO 21627-1 | |
| 15 | Moisture Content by Karl Fischer | IS 2362 -1993 | |
| 16 | Total Acid Number | DIN EN ISO 3682 | |
| 17 | Loss on ignition of Reinforced resins | ASTM D2584 | |
| 18 | Isocyanate content | FF/TM-27 (Internal Test Method) | |
| 19 | Neutralization equivalent | FF/TM-65 (Internal Test Method) | |
| 20 | Saponifiable chlorine content /Easily Hydrolyzable Chlorine Content | ASTM D 1726 – 11 | |
| 21 | Chemical resistance to coatings | IS 6746-1972 | |
| 22 | Chemical resistance study of cured system | ASTM C 225-85- 2004 | |
| 23 | Ash Content | IS 101 (Part 8/Sec 3) -1993 | |
| 24 | Active Oxygen Content | FF/TM-76 | |
| 25 | Hydroxyl Value of Epoxy Resin | ISO 7142-2007(E) | |
| 26 | Hydroxyl Value of Polyester Resins & Polyols | ASTM E 222-10 | |
| 27 | Glass Transition Temperature | ASTM D 3418/ASTM E 1356 | |
| 28 | Thermal Conductivity | ASTM E 1952 | |
| 29 | Specific Heat | ASTM E 1952 | |
| 30 | Non Volatile Content & Volume Solids | IS 101 (Part 2/sec2)-1986 | |
| 31 | Fineness of grind | IS 101 (Part 3/ Sec 5)-R-2006 | |
| 32 | Oil Absorption for Pigments and Extenders | IS 33-1992 | |
| 33 | Ash Content | IS 101 (Part 8/ Sec 3)-R-2006 | |
| 34 | Metal Content | IS 8766-1978 | |
| 35 | Wet Opacity | IS 101 (Part 4/Sec-1)-1988 | |
| 36 | Melting Point & range | IS 5762-1970 | |
| 37 | Distillation Range | ASTM D 85-02 | |
| 38 | Density by using Hydrometer | ASTM E 100 | |
| 39 | Chemical Resistance of coatings | IS 6746-1972 | |
| 40 | Particle Size of Residue on Sieves | IS 33-1992; IS 101 (Part 8/sec 1)-1989 | |
| 41 | Bulk Density | IS 33-1992 | |
| 42 | Loose Pack Density | IS 33-1992 | |
| 43 | Flash Point | ASTM D 93 | |
| 44 | Glass Content | IS 101 (Part 8 /Sec 3)-R-2006 | |
| 45 | Dry Film Thickness | IS 101 (Part 3/Sec 2)- R-2006 | |
| 46 | The resistance to water of a paint | IS 101 (Part 7/Sec 1) – R-2006 | |
| 47 | The resistance to single-coat paint films,paint systems or allied products to the action of liquids | IS 101 (Part 7/Sec 2) – R-2006 ; IEC 464-Part 2-1974 | |
| 48 | Ash Content | IS 101 (Part 8/Sec 3) – R-2006 | |
| 49 | pH of Pigments & Extenders | IS 33-1992 | |
| Reinforcement (Carbon fibre) | 1 | Density of carbon fibers by liquid displacement | TORAYCA-TY-030B-02 |
| 2 | Sizing amount of carbon fibers by pyrolysis | TORAYCA-TY-030B-05 |